VELOSIT® TDS-CW-111-EN_2319 (High Strenght Crystalline Waterproofing Slurry)

Public Channel / Data Sheets

Applica'on fields
VELOSIT CW 111 is a crystalline waterproofing slurry
for concrete substrates. It is very economic and easy
to apply. VELOSIT CW 111 becomes part of the
concrete and creates a waterproof layer inside the
concrete itself. It is especially strong against negaCve
side water pressure. Typical applicaCon fields
besides others are as follows:
• Waterproofing of basements and below grade
parking structures
• Waterproofing of potable water structures
• ProtecCon of dams and spill-ways
• Waterproofing of sewage structures
• Waterproofing of tunnels and pipelines
• Slab waterproofing (dry shake applicaCon)
• Waterproofing of elevator pits
Proper'es
VELOSIT CW 111 is a crystalline waterproofing slurry
with unsurpassed strength development.
VELOSIT CW 111 cures a lot faster than the current
standard products eliminaCng the need for days of
water curing and protecCon. VELOSIT CW 111
creates a reacCve layer inside the concrete that
allows the structure to self-heal shrinkage cracks
under contact with water.
VELOSIT CW 111 surpasses the requirements of EN
1504-3 for concrete repair (CR) and can be used
according to the principles 3.1 and 3.3 acc. to EN
1504-9.
VELOSIT CW 111 can be applied by brush, dry-shake
or suitable spray equipment.
• Self healing properCes of up to 0.4 mm staCc
cracks
• Unsurpassed strength development with more
than 20 MPa (2900 psi) aVer 24 h and more
than 50 MPa (7250 psi) aVer 28 days
• Open to foot traffic aVer 4 hours
• Extreme adhesive strength (concrete failure)
• Shrinkage compensated, no spider-web cracking
• Water curing only under hot and dry condiCons
required for 4 hours

pH range of 3-12 and against soV water with
low ion content
• Good weathering resistance
• Potable water approved
• Good sulfate resistance
Applica'on
1.) Substrate prepara'on
VELOSIT CW 111 can only be used on concrete
substrates.
a.) Hardened concrete must be prepared with sand
blasCng, shot blasCng or ideally high pressure water
blasCng (>100 bar/1450 psi) to remove all bond
breaking substances. Substrate must be pore open
and load bearing. The minimum requirement for
adhesive strength is 1 MPa (145 psi) and for the
compressive strength 20 MPa (2900 psi). AcCve
water leaks must be treated and fully stopped with
VELOSIT PC 221. Leaking cracks need to be sealed
with a PU injecCon material. Fill all blowholes,
honeycombs or other surface defects with
VELOSIT RM 211. Before the applicaCon of
VELOSIT CW 111, dampen the substrate with clean
water to a saturated surface dry (SSD) condiCon.
b.) Cold joints can be treated by chiseling out
approx. 5 cm (2“) concrete in a U shape around the
joint. Fill the opening with VELOSIT RM 211 and
finish with VELOSIT CW 111.
c.) Fresh concrete can be treated with
VELOSIT CW 111 in a dry-shake applicaCon. The
concrete must have sufficiently sCffened that a
helicopter trowel can work on it. Do not use any
curing compounds or other bond breaking materials
before applying VELOSIT CW 111.
2.) Processing
a.) Brush applicaCon: Mix VELOSIT CW 111 with 22–
23 % potable water, i.e. 5.50 – 5.75 l (1.45 – 1.5 gal.)
water per 25 kg (55 lb.) bag. Fill the complete mixing
water into a suitable bucket and mix the powder
with a slow speed drill (300 – 600 rpm) into the
water unCl a lump-free mix with a consistency of an
oil paint is achieved. With hard water (high Calcium
content) a slight false seing within the first 2 min.
aVer mixing is possible. In such case, re-mix for
another 30 seconds. Do not add water!
The product is workable for 30 – 45 min. at 23 °C.
Apply the first coat with a masons brush in crossing
applicaCons to the pre-dampened substrate at the
specified rate. The second coat must be applied
within the recoat Cme, which is 60 – 90 min. at
23 °C. If too much Cme elapses aVer applicaCon of
the first coat, a reduced bond between the layers
may be the result.
b.) Spray applicaCon: Use suitable spray
machines such as:
- Inotec GmbH: INOMAT-M8
- HighTech GmbH: HighPump Small
- Desoi GmbH: Desoi SP-Y
Prepare the product as described for the brush
applicaCon under a.). The water addiCon may
be reduced slightly to get a more thixotropic
mix. Fill the product into the feed hopper of
the spray machine and spray conCnuously. If
less water is used the whole specified amount
of VELOSIT CW 111 may be applied in one liV.
Otherwise spray in two layers with a wait Cme
of approx. 30 min. between coats. Long spray

interrupCons may result in clogging of the spray
hose. The product may cure a lot faster if
the hose is exposed to direct sunlight. Always empty
and flush the machine aVer spraying or before long
spray interrupCons. VELOSIT CW 111 is a fast curing
material and may be hard to remove if leV in the
machine.
c.) Dry-shake applicaCon: VELOSIT CW 111 can be
applied in powder form onto fresh concrete before
finishing the surface. The product is applied
uniformly onto the concrete and then finished with
a helicopter trowel. Make sure that the trowel forces
sufficient moisture to the surface to completely wet
and embed the powdered VELOSIT CW 111.
3.) Curing
VELOSIT CW 111 does not require long term curing
as it reacts relaCvely fast with water. Only under hot
weather or very dry condiCons water curing for 3 – 4
hours is required.
Please consider for the dry shake applicaCon that
the concrete may require curing. Take the required
steps by either water curing as specified or applying
a curing compound.
Es'ma'ng
Waterproofing concrete:
Brush applicaCon
1st coat VELOSIT CW 111: 0.8 kg/m2
2nd coat VELOSIT CW 111: 0.7 kg/m2
Spray applicaCon
VELOSIT CW 111: 1.5 kg/m2
Dry-Shake applicaCon
VELOSIT CW 111: 1.2 kg/m2
Cleaning
VELOSIT CW 111 can be removed in the fresh state
with water. Once it has cured acidic cleaners like
muriaCc acid are required.
Quality features
Color: gray
Mixing raCo by weight: 100 : 23
Mixing raCo by volume: 100 : 28
Density: 1.2 kg/l
Substrate temperature: 5 – 35 °C
(40 – 95 °F)
Service temperature: -18 – 97 °C
(0 - 207 °F)
Water impermeability acc. EN 12390-8:
- PosiCve side: 13 bar (190 psi)
- NegaCve side: 13 bar (190 psi)
Compressive / flexural strength:
4 hours: 8 / 1 MPa (1160/145 psi)
24 hours: 21 / 4 MPa (3045/580 psi)
7 days: 35 / 5 MPa (5075/725 psi)
28 days: 51 / 7 MPa (7395/1015 psi)
Chloride ions: < 0.05 %
CarbonaCon resistance: passed
Capillary water absorpCon: 0.4 kg/m2 x h0,5
Adhesive strength: 2.8 MPa (406 psi)
(concrete failure)
Restrained shrinkage: 2.8 MPa (406 psi)
(concrete failure)
Fire raCng EN13501-1: Class A1
Packaging
VELOSIT CW 111 is available in 25 kg (55 lb.)
waterCght plasCc bags.
Storage
VELOSIT CW 111 can be stored in unopened original
packs for 12 months at 5 – 35 °C (40 – 95 °F) in a dry
storage place protected against sunlight.
Safety
Please observe the actual valid material safety data
sheet and follow the described safety measures for
handling of the product.
Used product containers must be empCed
completely aVer use. They can be returned to
VELOSIT GmbH & Co. KG on request.
Recommenda'ons
VELOSIT CW 111 is only available for professional
applicators.
The crystalline waterproofing principle requires
several days of water contact to develop its full
effect.
VELOSIT CW 111 may discolor or show strong
efflorescence in water contact. This is normal and
caused by the crystalline reacCon.
All described product features are determined under
controlled laboratory condiCons according to the
relevant internaConal standards. Values determined
under job site condiCons may deviate from the
stated values.
Please always use the latest version of this data
sheet available from our website www.velosit.de.
Manufacturer
VELOSIT GmbH & Co. KG
Industriepark 7
32805 Horn-Bad Meinberg
Germany
www.velosit.de
+971600541110
https://wa.me/97172281030
+971 2 566 2610

Share on Social Networks

Share Link

Use permanent link to share in social media

Share with a friend

Please login to send this document by email!

Embed in your website

Select Link to start with 

4. VELOSIT ® CW 111 Used product containers must be empCed completely aVer use. They can be returned to VELOSIT GmbH & Co. KG on request. Recommenda'ons VELOSIT CW 111 is only available for professional applicators. The crystalline waterproofing principle requires several days of water contact to develop its full effect. VELOSIT CW 111 may discolor or show strong efflorescence in water contact. This is normal and caused by the crystalline reacCon. All described product features are determined under controlled laboratory condiCons according to the relevant internaConal standards. Values determined under job site condiCons may deviate from the stated values. Please always use the latest version of this data sheet available from our website www.velosit.de . Manufacturer VELOSIT GmbH & Co. KG Industriepark 7 32805 Horn-Bad Meinberg Germany www.velosit.de 2319 page of 4 4 VELOSIT GmbH & Co. KG Industriepark 7 D-32805 Horn-Bad Meinberg 19 VELOSIT CW 111 DIN EN 1504-3 Product for Structural and non structural repair for concrete Compressive strength R3 Chloride ion content ≤ 0.05 % Adhesive bond ≥ 1.5 MPa Restrained shrinkage/ NPD expansion Reaction to fire E

1. VELOSIT ® CW 111 Applica'on fields VELOSIT CW 111 is a crystalline waterproofing slurry for concrete substrates. It is very economic and easy to apply. VELOSIT CW 111 becomes part of the concrete and creates a waterproof layer inside the concrete itself. It is especially strong against negaCve side water pressure. Typical applicaCon fields besides others are as follows: • Waterproofing of basements and below grade parking structures • Waterproofing of potable water structures • ProtecCon of dams and spill-ways • Waterproofing of sewage structures • Waterproofing of tunnels and pipelines • Slab waterproofing (dry shake applicaCon) • Waterproofing of elevator pits Proper'es VELOSIT CW 111 is a crystalline waterproofing slurry with unsurpassed strength development. VELOSIT CW 111 cures a lot faster than the current standard products eliminaCng the need for days of water curing and protecCon. VELOSIT CW 111 creates a reacCve layer inside the concrete that allows the structure to self-heal shrinkage cracks under contact with water. VELOSIT CW 111 surpasses the requirements of EN 1504-3 for concrete repair (CR) and can be used according to the principles 3.1 and 3.3 acc. to EN 1504-9. VELOSIT CW 111 can be applied by brush, dry-shake or suitable spray equipment. • Self healing properCes of up to 0.4 mm staCc cracks • Unsurpassed strength development with more than 20 MPa (2900 psi) aVer 24 h and more than 50 MPa (7250 psi) aVer 28 days • Open to foot traffic aVer 4 hours • Extreme adhesive strength (concrete failure) • Shrinkage compensated, no spider-web cracking • Water curing only under hot and dry condiCons required for 4 hours 2319 page of 1 4 VELOSIT ® CW 111 High Strength Crystalline Waterproofing slurry

2. VELOSIT ® CW 111 • Good resistance against aggressive media with a pH range of 3-12 and against soV water with low ion content • Good weathering resistance • Potable water approved • Good sulfate resistance Applica'on 1.) Substrate prepara'on VELOSIT CW 111 can only be used on concrete substrates. a.) Hardened concrete must be prepared with sand blasCng, shot blasCng or ideally high pressure water blasCng (>100 bar/1450 psi) to remove all bond breaking substances. Substrate must be pore open and load bearing. The minimum requirement for adhesive strength is 1 MPa (145 psi) and for the compressive strength 20 MPa (2900 psi). AcCve water leaks must be treated and fully stopped with VELOSIT PC 221. Leaking cracks need to be sealed with a PU injecCon material. Fill all blowholes, honeycombs or other surface defects with VELOSIT RM 211. Before the applicaCon of VELOSIT CW 111, dampen the substrate with clean water to a saturated surface dry (SSD) condiCon. b.) Cold joints can be treated by chiseling out approx. 5 cm (2“) concrete in a U shape around the joint. Fill the opening with VELOSIT RM 211 and finish with VELOSIT CW 111. c.) Fresh concrete can be treated with VELOSIT CW 111 in a dry-shake applicaCon. The concrete must have sufficiently sCffened that a helicopter trowel can work on it. Do not use any curing compounds or other bond breaking materials before applying VELOSIT CW 111. 2.) Processing a.) Brush applicaCon: Mix VELOSIT CW 111 with 22– 23 % potable water, i.e. 5.50 – 5.75 l (1.45 – 1.5 gal.) water per 25 kg (55 lb.) bag. Fill the complete mixing water into a suitable bucket and mix the powder with a slow speed drill (300 – 600 rpm) into the water unCl a lump-free mix with a consistency of an oil paint is achieved. With hard water (high Calcium content) a slight false seing within the first 2 min. aVer mixing is possible. In such case, re-mix for another 30 seconds. Do not add water! The product is workable for 30 – 45 min. at 23 °C. Apply the first coat with a masons brush in crossing applicaCons to the pre-dampened substrate at the specified rate. The second coat must be applied within the recoat Cme, which is 60 – 90 min. at 23 °C. If too much Cme elapses aVer applicaCon of the first coat, a reduced bond between the layers may be the result. b.) Spray applicaCon: Use suitable spray machines such as: - Inotec GmbH: INOMAT-M8 - HighTech GmbH: HighPump Small - Desoi GmbH: Desoi SP-Y Prepare the product as described for the brush applicaCon under a.). The water addiCon may be reduced slightly to get a more thixotropic mix. Fill the product into the feed hopper of the spray machine and spray conCnuously. If less water is used the whole specified amount of VELOSIT CW 111 may be applied in one liV. Otherwise spray in two layers with a wait Cme of approx. 30 min. between coats. Long spray 2319 page of 2 4 

 Negativabdichtung Kelleraußenwand Bodenniveau     CW  

3. VELOSIT ® CW 111 interrupCons may result in clogging of the spray hose. The product may cure a lot faster if the hose is exposed to direct sunlight. Always empty and flush the machine aVer spraying or before long spray interrupCons. VELOSIT CW 111 is a fast curing material and may be hard to remove if leV in the machine. c.) Dry-shake applicaCon: VELOSIT CW 111 can be applied in powder form onto fresh concrete before finishing the surface. The product is applied uniformly onto the concrete and then finished with a helicopter trowel. Make sure that the trowel forces sufficient moisture to the surface to completely wet and embed the powdered VELOSIT CW 111. 3.) Curing VELOSIT CW 111 does not require long term curing as it reacts relaCvely fast with water. Only under hot weather or very dry condiCons water curing for 3 – 4 hours is required. Please consider for the dry shake applicaCon that the concrete may require curing. Take the required steps by either water curing as specified or applying a curing compound. Es'ma'ng Waterproofing concrete: Brush applicaCon 1 st coat VELOSIT CW 111: 0.8 kg/m 2 2 nd coat VELOSIT CW 111: 0.7 kg/m 2 Spray applicaCon VELOSIT CW 111: 1.5 kg/m 2 Dry-Shake applicaCon VELOSIT CW 111: 1.2 kg/m 2 Cleaning VELOSIT CW 111 can be removed in the fresh state with water. Once it has cured acidic cleaners like muriaCc acid are required. Quality features Color: gray Mixing raCo by weight: 100 : 23 Mixing raCo by volume: 100 : 28 Density: 1.2 kg/l Substrate temperature: 5 – 35 °C (40 – 95 °F) Service temperature: -18 – 97 °C (0 - 207 °F) Water impermeability acc. EN 12390-8: - PosiCve side: 13 bar (190 psi) - NegaCve side: 13 bar (190 psi) Compressive / flexural strength: 4 hours: 8 / 1 MPa (1160/145 psi) 24 hours: 21 / 4 MPa (3045/580 psi) 7 days: 35 / 5 MPa (5075/725 psi) 28 days: 51 / 7 MPa (7395/1015 psi) Chloride ions: < 0.05 % CarbonaCon resistance: passed Capillary water absorpCon: 0.4 kg/m 2 x h 0,5 Adhesive strength: 2.8 MPa (406 psi) (concrete failure) Restrained shrinkage: 2.8 MPa (406 psi) (concrete failure) Fire raCng EN13501-1: Class A1 Packaging VELOSIT CW 111 is available in 25 kg (55 lb.) waterCght plasCc bags. Storage VELOSIT CW 111 can be stored in unopened original packs for 12 months at 5 – 35 °C (40 – 95 °F) in a dry storage place protected against sunlight. Safety Please observe the actual valid material safety data sheet and follow the described safety measures for handling of the product. 2319 page of 3 4

Views

  • 5532 Total Views
  • 4229 Website Views
  • 1303 Embeded Views

Actions

  • 0 Social Shares
  • 5
  • 0
  • 0 Comments

Share count

  • 0  Facebook
  • 0  Twitter
  • 0  LinkedIn

Embeds 8

  • 1 www.sab-cs.com
  • 20 161.97.92.48
  • 1 sab-cs.com
  • 187 www.sab-us.com
  • 1 google.com
  • 6 161.97.92.48:8011
  • 154 www.google.com
  • 8

Website Visitors - 503607